Specification and Application
TYPE |
Size |
Description |
Characterisic and Application |
651-0615F |
15-45 |
WC-Co 94/06 Agglomerated Sintered |
。HVOF APS 。fine WC 。Used for drawing equipment etc. 。Service temperature up to 500℃ 。higher resistance to abrasion and corrosion resistance by low Co 。lower hardness ,strength and than WC88/12 。high bone strength 。Low Oxidation and corrosion resistance |
651-1215 |
15-45 |
WC-Co88/12 |
。HVOF HVAF APS 。median WC 。Service temperature up to 500℃ 。Used for oil field apparetus, wire drawing equipment, fan and compressor blades,pump seals and housing, machine parts etc 。Hard and densen coating with high resistance to abrasion and erosion。Good bond strength 。High Oxidation and corrosion resistance |
651-1215F 651-1210F 652-1215F 654-1245F |
15-45 10-33 15-53 45-75 |
WC-Co88/12 |
。HVOF APS 。fine WC 。higher density 。（see651-1215） |
651-1215N 651-1210N 652-1215N 654-1245N |
15-45 10-33 15-53 45-75 |
WC-Co88/12 |
。HVOF APS 。nano size WC 。higher resistance to abrasion and corrosion resistance 。（see651-1215） |
651-1715
|
15-45 |
WC-Co88/17 |
。HVOF HVAF APS 。median WC 。Service temperature up to 500℃ 。Used for turbine applications, extrusion dies,glass industry ,paper mill roll,pump parts,etc.. 。Higher ductility due to higher Co content than WC-Co 88/12 。Hard and densen coating with high resistance to abrasion 。High sliding wear and erosion resistance 。Good bond strength 。High Oxidation and corrosion resistance |
651-1715F |
15-45 |
WC-Co88/17 |
。HVOF 。fine WC 。higher resistance to abrasion 。（see651-1715） |
653-0415 654-0445
|
15-45 45-75 |
WC-Co86/10/4 |
。 HVAF HVOF APS 。median WC 。Service temperature up to 500℃ 。Used for paper rolls,gate and ball valves, hydraulic cylinders,compressor shafts ,etc 。Hard chrome replacement 。The CoCr matrix shows higher corrosion and abrasion resistance than the Co matrix 。Useable in water based solutions and wet corrosive environments 。Smooth coatings with fone microstructure and high bond strengths |
651-0410F 651-0415F 654-0445F |
10-33 15-45 45-75 |
WC-Co86/10/4 |
。HVOF HVAF APS 。fine WC 。Higher corrosion resistance 。（see653-0415） |
651-0410N 651-0415N 654-0445N |
10-33 15-45 45-75 |
WC-Co86/10/4 |
。HVOF HVAF APS 。nano size WC 。higher density bone strength 。（see 653-0415） |
671-1015F 671-1020F
|
15-53 20-53 |
WC-Ni90/10 Agglomerated Sintered |
。HVOF 。fine WC 。Service temperature up to 500℃ 。Higher corrosion resistance than WC/Co |
671-1515F 671-1520F
|
15-53 20-53 |
WC-Ni85/15 Agglomerated Sintered |
。HVOF 。（see 671-1015） 。Higher ductility |
671-1715F 671-1720F
|
15-53 20-53 |
WC-Ni83/17 Agglomerated Sintered |
。HVOF 。（see671-1015），Higher ductility |
681-2715F
|
15-45 |
WC-Cr3C2-Ni73/20/7 |
。HVOF HVAF 。fine WC 。Service temperature up to 750℃ 。Used for gate valves .etc 。Higher oxidation and corrosion resistance 。Smooth coatings with fone microstructure and high bond strengths |
871-2510 871-2522 871-2515
|
10-38 22-45 15-45 |
Cr3C2-NiCr75/25 |
。HVOF 。median WC 。Service temperature up to 870℃ 。Used for valve handle,turbine applications and fuel rod etc 。High erosion and corrosion resistance with dense coating 。High resistance to activation ,sliding wear and hot gas corrosion |
871-2005 |
5-45 |
Cr3C2-NiCr80/20 |
。HVOF 。Service temperature up to 870℃ 。（see 791-2510） 。hardness ≥75/25 |