텅스텐 파우더 프레스 준비
학년 |
ISO 등급 |
화학 조성 (중량 %) |
분말 특성 |
소결 된 물성 |
||||||||||
WC |
Co |
TiC |
TaC |
기타 |
T.C |
윤활유 |
평균 |
겉보기 밀도 g/cm3 |
흐름 |
경도 HRA±0.5 |
밀도 |
TRS |
||
CTF40D |
- |
88.0 |
12.0 |
- |
- |
- |
5.32 |
2.0%밀랍 |
6.0 |
3.20 |
27 |
87.5 |
14.30 |
2800 |
CTD20A |
- |
91.0 |
9.0 |
- |
- |
- |
5.56 |
2.0%PEG |
8.0 |
3.70 |
25 |
86.5 |
14.60 |
2500 |
CTT20A |
P20 |
79.3 |
8.0 |
8.7 |
4.0 |
- |
6.82 |
2.0%밀랍 |
2.0 |
2.70 |
30 |
91.8 |
12.40 |
2200 |
CTK10F |
K10 |
93.3 |
6.5 |
- |
- |
0.20 |
5.76 |
2.0%밀랍 |
1.8 |
3.40 |
27 |
92.0 |
14.86 |
3200 |
CTK30F |
K30 |
91.1 |
8.5 |
- |
- |
0.4 |
5.63 |
2.0%밀랍 |
1.8 |
3.10 |
29 |
91.0 |
14.65 |
2800 |
CTK50 |
K50 |
90.0 |
10.0 |
- |
- |
- |
5.52 |
2.0%밀랍 |
1.8 |
3.20 |
28 |
90.5 |
14.54 |
2800 |
CTF05 |
K02 |
97.0 |
3.0 |
- |
- |
- |
5.98 |
2.0%밀랍 |
4.0 |
3.35 |
25 |
92.0 |
15.25 |
2100 |
CTD22 |
- |
90.8 |
9.2 |
- |
- |
- |
5.55 |
2.0%밀랍 |
4.0 |
3.20 |
28 |
88.4 |
14.62 |
2600 |
CTU15F |
K10-K30 |
91.4 |
8.0 |
- |
- |
0.6 |
5.76 |
2.0%밀랍 |
0.6 |
3.00 |
28 |
93.0 |
14.65 |
4200 |
CTU25UF |
K10-K50 |
86.0 |
12.0 |
- |
- |
1.4 |
5.49 |
2.0%밀랍 |
0.4 |
2.70 |
30 |
93.0 |
14.10 |
4000 |
CTU10 |
K10 |
93.85 |
6.0 |
- |
- |
0.15 |
5.84 |
2.0%밀랍 |
0.8 |
3.05 |
27 |
93.0 |
14.85 |
2700 |
CTU20 |
K10-K20 |
89.5 |
10.0 |
- |
- |
0.5 |
5.57 |
2.0%밀랍 |
0.8 |
2.85 |
30 |
91.8 |
14.45 |
3400 |
CTU30 |
K20-K30 |
85.7 |
13.5 |
- |
- |
0.8 |
5.38 |
2.0%밀랍 |
0.8 |
2.70 |
32 |
90.5 |
14.00 |
3500 |
CTK02 |
K01 |
95.9 |
4.0 |
- |
- |
0.1 |
5.92 |
2.0%밀랍 |
1.3 |
3.40 |
24 |
92.7 |
15.15 |
2100 |
CTK05 |
K05 |
94.0 |
6.0 |
- |
- |
- |
5.79 |
2.0%밀랍 |
1.5 |
3.40 |
24 |
92.0 |
14.90 |
2450 |
CTK10 |
K10 |
94.0 |
6.0 |
- |
- |
- |
5.78 |
2.0%밀랍 |
2.0 |
3.40 |
26 |
91.5 |
14.90 |
2500 |
CTK20 |
K20 |
94.0 |
6.0 |
- |
- |
- |
5.79 |
2.0%밀랍 |
3.0 |
3.40 |
27 |
91.0 |
14.90 |
2600 |
CTK30 |
K30 |
92.0 |
8.0 |
- |
- |
- |
5.64 |
2.0%밀랍 |
3.0 |
3.35 |
28 |
90.0 |
14.70 |
2700 |
CTK40 |
K40 |
91.0 |
9.0 |
- |
- |
- |
5.57 |
2.0%밀랍 |
3.0 |
3.20 |
29 |
89.5 |
14.60 |
2800 |
CTF20D |
- |
94.0 |
6.0 |
- |
- |
- |
5.76 |
2.0%밀랍 |
4.0 |
3.40 |
26 |
90.0 |
14.90 |
2600 |
CTF25D |
- |
92.0 |
8.0 |
- |
- |
- |
5.63 |
2.0%밀랍 |
5.0 |
3.40 |
26 |
89.5 |
14.70 |
2800 |
CTF31 |
- |
90.5 |
9.5 |
- |
- |
- |
5.59 |
2.0%밀랍 |
4.0 |
3.30 |
26 |
89 |
14.43 |
2800 |
CTF40 |
- |
88.0 |
12.0 |
- |
- |
- |
5.40 |
2.0%밀랍 |
2.0 |
3.10 |
27 |
89.0 |
14.40 |
3000 |
CTF45 |
- |
87.0 |
13.0 |
- |
- |
- |
5.34 |
2.0%밀랍 |
2.5 |
3.05 |
30 |
88.5 |
14.20 |
3100 |
CTF50 |
- |
85.0 |
15.0 |
- |
- |
- |
5.20 |
2.0%밀랍 |
3.5 |
2.90 |
30 |
87.5 |
14.00 |
3000 |
CTF60 |
- |
80.0 |
20.0 |
- |
- |
- |
4.91 |
2.0%밀랍 |
5.5 |
2.75 |
32 |
84.5 |
13.65 |
2700 |
CTF65 |
- |
78.0 |
22.0 |
- |
- |
- |
4.78 |
2.0%밀랍 |
5.5 |
2.70 |
33 |
84.0 |
13.40 |
2700 |
CTF70 |
- |
75.0 |
25.0 |
- |
- |
- |
4.60 |
2.0%밀랍 |
5.5 |
2.65 |
33 |
82.5 |
13.18 |
2400 |
CTD10 |
- |
94.0 |
6.0 |
- |
- |
- |
5.77 |
2.0%밀랍 |
8.0 |
3.40 |
26 |
89.0 |
14.95 |
2500 |
CTD20 |
- |
92.0 |
8.0 |
- |
- |
- |
5.64 |
2.0%밀랍 |
8.0 |
3.40 |
26 |
86.5 |
14.60 |
2500 |
CTD25A |
- |
90.0 |
10.0 |
- |
- |
- |
5.51 |
2.0%밀랍 |
3.0 |
3.30 |
26 |
88.5 |
14.50 |
2850 |
CTD50 |
- |
85.0 |
15.0 |
- |
- |
- |
5.20 |
2.0%밀랍 |
6.0 |
3.20 |
27 |
86.0 |
14.00 |
3000 |
CTT20 |
P20 |
72.0 |
8.0 |
8.0 |
12.0 |
- |
6.86 |
2.0%밀랍 |
2.0 |
2.70 |
30 |
92.2 |
12.40 |
1900 |
CTT30 |
P30 |
75.8 |
8.0 |
6.2 |
10.0 |
- |
6.60 |
2.0%밀랍 |
2.0 |
2.80 |
28 |
91.5 |
12.80 |
2100 |
| Chinatungsten 온라인 초경 카바이드. 그만큼 제품의 제조에 널리 사용되는 프레스 분말 준비의 다양한 유형의 제품은 다음과 같은 특징이 있습니다 : |
| 1、안정된 겉보기 밀도 |
| 2、구형 분말의 우수한 유동성 덕분 |
| 3、좋은 압축률 |
| 4、화학적 순도가 높고 탄소 함유량을 잘 조절합니다. |
| 5、우리 RTP로 만든 초경합금은 우수한 물성을 지니고 있습니다. |